| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 61 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 57 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 62 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D 638 |
| Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2250 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 700 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 118 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 26 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 58 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, -40°C to 40°C, flow | 6.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 111 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 103 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 104 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 99 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 88 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Melt Flow Rate, 220°C/10.0 kgf | 30 | g/10 min | ASTM D 1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 27 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 18 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 138 | Pa-s | ISO 11443 |
| ELECTRICAL | Value | Unit | Standard |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-1 Flame Class Rating (3) | 1.2 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 |
| UL Recognized, 94-5VB Rating (3) | 2 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 0.8 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 0.8 mm | 850 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 2.0 mm | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index (LOI) | 30 | % | ISO 4589 |
| Source GMD, last updated:2009/07/20 | | |