| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 54 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 45 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 2.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 8.5 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2870 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 85 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2930 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 52 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 42 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 2.7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 14 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3060 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 77 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2790 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 21 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 3 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 2 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 95 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 81 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 9.E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.02E+02 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 9.3E+01 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.04E+02 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 97 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 99 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.11 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 220°C/10.0 kgf | 9.2 | g/10 min | ASTM D 1238 |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.8 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 8 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:01/09/2006 | | |
| Processing | | | |