| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 155 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 38 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 30 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 2.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1900 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 50 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1900 | MPa | ISO 178 |
| Hardness, H358/30 | 70 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 95 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.21 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 86 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 91 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 88 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 75 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.7 | % | S-Plastics Method |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.55 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 7 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 8 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >0.E+00 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >0.E+00 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 5.2 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.2 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.15 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.026 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1 | mm | UL 94 by GE |
| UL Compliant, 94HB Flame Class Rating 2nd value (3)(4) | 3 | mm | UL 94 by GE |
| Glow Wire Flammability Index 750°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 19 | % | ISO 4589 |
| Source GMD, last updated:06/25/2003 | | |