| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 63 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 59 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 66 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | >100 | % | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | >100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2590 | MPa | ASTM D 638 |
| Tensile Stress, yield, 5 mm/min | 62 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4.3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | >50 | % | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2520 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 93 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2510 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 385 | J/m | ASTM D 256 |
| Izod Impact, notched, 0°C | 290 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, -30°C to 80°C, flow | 6.9E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 7.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 111 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 102 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 104 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 99 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 88 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.6 | % | S-Plastics Method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.6 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 13 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94-5VB Rating (3)(4) | 2.3 | mm | UL 94 by GE |
| UL Recognized, 94V-2 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 2 | mm | UL 94 |
| UL Recognized, 94-5VB Rating (3) | 2.3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 29 | % | ISO 4589 |
| Source GMD, last updated:02/01/2005 | | |