| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 49 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2680 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2750 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 48 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.2 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 77 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2900 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 3 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 0 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 43 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 17 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 89 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 108 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 109 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 93 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.16 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 220°C/10.0 kgf | 8.3 | g/10 min | ASTM D 1238 |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.25 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 7 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:01/09/2006 | | |